Ti-6AI-4V grade 5

Contact an AP&C powder specialist

For over a decade, experienced users of additive manufacturing, MIM, HIP, and coating technologies have trusted AP&C’s Ti-6Al-4V powders to build high-quality components for the Aerospace, Biomedical, and Industrial markets; because, high-quality components begin with high-quality powders.

AP&C’s Ti-6Al-4V powders are manufactured using the proprietary Advanced Plasma Atomization (APATM ) process, producing powders with the ideal characteristics for any application, including additive manufacturing. These highly spherical powders contain virtually no entrapped porosities. Additionally, they possess minimal satellite content, resulting in truly exceptional flowability and packing density.

Titanium alloy: Ti-6Al-4V grade 5

Powder chemistry may comply with standards: ASTM B348, ASTM F136, ASTM F1580, ASTM F2924, ASTM F3001, AMS 1498
Typical particle size distributions (PSD): 0-20 μm, 15-45 μm, 15-63 μm, 45-106 μm, 45-150 μm, 106-180 μm

SD Size distribution by laser diffraction (ASTM B822) Apparent density (ASTM B212) Flow rate (ASTM B213) Oxygen content
   D10  D50  D90      
 0-20 µm  6 µm  13 µm  19 µm  2.8 g/cm3*   -  0.19 %
 15-45 µm  20 µm  34 µm  44 µm  2.49 g/cm3  28 s  0.16 %
 15-53 µm  23 µm  38 µm  52 µm  2.51 g/cm3  26 s  0.16 %
 20-63 µm  24 µm  44 µm  61 µm  2.50 g/cm3  25 s  0.15 %
 45-106 µm  52 µm  71 µm  102 µm  2.47 g/cm3  25 s  0.13 %
 45-150 µm  54 µm  81 µm  123 µm  2.59 g/cm3  25 s  0.13 %

*Tap density per ASTM B527

Ti-6AI-4V Grade 5

Particle size distribution is measured by laser diffraction as per ASTM B822.  Due to the high sphericity and very low satellites present on AP&C powder, the particle size distribution is highly uniform and the D10, D50 and D90 meet and exceed the industry requirements with an exceptional batch to batch reliability. The typical powder atomization yield ranges from 0-150 µm, after atomization, the powder is sieved according customer specifications.